Feasibility of using ultrasonic-based prediction for hydrogen embrittlement susceptibility of high-strength heat-resistant steel 2.25Cr-1Mo-0.25V
Dongdong Ye, Changdong Yin, Zhou Xu, Jianjun Chen, Yiwen Wu, Jiabao Pan, Guiling Zeng, Huachao Xu, Rui Li
Topics & Concepts
Hydrogen embrittlementMaterials scienceUltrasonic sensorUltrasonic testingHydrogenNondestructive testingSIGNAL (programming language)EmbrittlementUltimate tensile strengthNuclear engineeringComposite materialAcousticsMetallurgyCorrosionComputer scienceEngineeringOrganic chemistryChemistryMedicineRadiologyPhysicsProgramming languageHydrogen embrittlement and corrosion behaviors in metalsFatigue and fracture mechanicsMaterial Properties and Failure Mechanisms