Age hardening in superhard ZrB2-rich Zr1-xTaxBy thin films
Babak Bakhit, Justinas Pališaitis, Zhengtao Wu, Maurício A. Sortica, Daniel Primetzhofer, Per O. Å. Persson, Johanna Rosén, Lars Hultman, I. Petrov, J. E. Greene, Grzegorz Greczyński
Abstract
We recently showed that sputter-deposited Zr1-xTaxBy thin films have hexagonal AlB2-type columnar nanostructure in which column boundaries are B-rich for x < 0.2, while Ta-rich for x ≥ 0.2. As-deposited layers with x ≥ 0.2 exhibit higher hardness and, simultaneously, enhanced toughness. Here, we study the mechanical properties of ZrB2.4, Zr0.8Ta0.2B1.8, and Zr0.7Ta0.3B1.5 films annealed in Ar atmosphere as a function of annealing temperature Ta up to 1200 °C. In-situ and ex-situ nanoindentation analyses reveal that all films undergo age hardening up to Ta = 800 °C, with the highest hardness achieved for Zr0.8Ta0.2B1.8 (45.5±1.0 GPa). The age hardening, which occurs without any phase separation or decomposition, can be explained by point-defect recovery that enhances chemical bond density. Although hardness decreases at Ta > 800 °C due mainly to recrystallization, column coarsening, and planar defect annihilation, all layers show hardness values above 34 GPa over the entire Ta range.