Hierarchical Characteristics of Hydrogen-Assisted Crack Growth and Microstructural Strain Evolution in Tempered Martensitic Steels: Case of Quasi-cleavage Fracture
Tingshu Chen, Takahiro Chiba, Motomichi Koyama, Akinobu Shibata, Eiji Akiyama, Kenichi Takai
Topics & Concepts
Materials scienceLathCrack closureMartensiteCrack growth resistance curvePlasticityComposite materialCrack tip opening displacementNucleationCoalescence (physics)Fracture mechanicsMicrostructureMetallurgyChemistryAstrobiologyOrganic chemistryPhysicsHydrogen embrittlement and corrosion behaviors in metalsMicrostructure and Mechanical Properties of SteelsMaterial Properties and Failure Mechanisms