Influence of heat treatments on the susceptibility of 9%Ni low carbon steel to sulfide stress corrosion cracking
Rachel Pereira Carneiro da Cunha, Cássio Barbosa, R.F. Barrozo, Javier Velasco, Sérgio Souto Maior Tavares
Topics & Concepts
TemperingQuenching (fluorescence)Materials scienceMetallurgyStress corrosion crackingCarbon steelCarbon fibersSulfideCorrosionAusteniteScanning electron microscopeComposite materialMicrostructureFluorescencePhysicsComposite numberQuantum mechanicsHydrogen embrittlement and corrosion behaviors in metalsMicrostructure and Mechanical Properties of SteelsCorrosion Behavior and Inhibition