Preparation of glass-based composites with green upconversion and persistent luminescence using modified direct doping method
V. Lahti, Nirajan Ojha, Sami Vuori, Mika Lastusaari, Laëticia Petit
Abstract
New oxyfluorophosphate glass-based composites which exhibit not only green upconversion under 980 nm pumping but also green persistent luminescence (PeL) after being UV charged were successfully prepared using the direct doping method. The composites are composed of a glass-ceramic with Er 3+ doped CaF 2 crystals and of the persistent luminescent particles with the SrAl 2 O 4 :Eu,Dy composition. In the standard direct doping method, the glass melt is quenched few minutes after adding the PeL particles in the melt held at a temperature lower than the melting temperature. It is demonstrated that the direct doping method should be modified when preparing oxyfluoride glasses with PeL particles to limit not only the decomposition of the PeL particles in the glass but also the fluorine evaporation occurring during the glass preparation. Here, the composites were prepared by quenching the melt right after adding the PeL particles. The modified direct doping method allows the preparation of glass-based composites with strong green upconversion and homogeneous green persistent luminescence.