Well-Tunable, 3D-printable, and Fast Autonomous Self-Healing Elastomers
Bingrui Li, Sirui Ge, Xiao Zhao, Qiyi Chen, Jia Tian, Diana Hun, Alexei P. Sokolov, Tomonori Saito, Pengfei Cao
Abstract
Self-healing elastomers provide extended longevity of functional materials, due to their unique adaptability and durability. However, a major scientific challenge remains in developing materials with a rapid healing process combined with decent mechanical properties and a relatively simple synthesis approach. Herein, we report a versatile design approach on self-healing elastomer by incorporating two different hydrogen bonding containing monomers, i.e., 2-[[(butylamino)carbonyl]oxy]ethyl acrylate (BCOE) and 2-ureido-4[1H]pyrimidinone (UPy) functionalized ethyl methacrylate. Poly(BCOE-r-UPy)s are synthesized by reversible addition−fragmentation chain-transfer (RAFT) polymerization, and controlling the ratio of two monomers enables well-tunable mechanical properties with tensile strength ranging from 0.04 to 6.3 MPa and tensile strain up to 3,000%. The characteristic dissociation energy is calculated from a temperature dependence of terminal relaxation followed by subtracting the segmental relaxation. The rapid autonomous self-healing is achieved when the molar composition of Poly(BCOE-r-UPy) is tailored to BCOE/UPy = 99/1. The self-healing process is monitored in situ by a helium-ion microscope, and its macroscopic study using tensile tests indicates that Poly(BCOE-r-UPy1) with 1% molar ratio of UPy recovers 70% of its original toughness at ambient temperature within 10 mins. 3D printing of Poly(BCOE-r-UPy) affords a self-healable 3D structure, demonstrating the adaptability of Poly(BCOE-r-UPy) for on-demand fabrication. The simplicity of synthesis, well-tunable mechanical properties, unique self-healability, and 3D printing capability of Poly(BCOE-r-UPy)s indicate their potential toward a range of applications.