Enhancement of mechanical properties of hydroxyapatite coating prepared by electrophoretic deposition method
Nayereh Asgari, Masoud Rajabi
Abstract
Abstract The addition of bio‐inert ceramics such as alumina and zirconia can significantly improve the mechanical properties of hydroxyapatite bioactive coatings and increase their biocompatibility. In the present study, the surface of a titanium substrate was coated by the electrophoretic deposition method (EPD). Moreover, the reaction bonding process has been used to precipitate the nanocomposite containing the hydroxyapatite (HA), alumina, yitteria‐stabilized zirconia (YSZ). The coating process was performed by an electrical power supply and a suspension of hydroxyapatite, aluminum, and YSZ nanopowders. For preparing a suspension consisting of 50% isopropanol and 50% acetone, 0.6 g/L of iodine was used as a stabilizer. Green and sintered coatings were analyzed by FE‐SEM and XRD. In addition, the mechanical properties such as bonding strength, hardness, and toughness were measured. The hardness, bonding strength, and toughness of the HA coating were 107 ± 10.3 HV, 10.8 ± 3.2MPa, and 0.72MPa√m, respectively, while those of the HA‐Al 2 O 3 ‐YSZ nanocomposite coating were 213 ± 1.8 HV, 35 ± 1.6MPa, and 1.6MPa√m, respectively.