Concurrent Amorphization and Nanocatalyst Formation in Cu‐Substituted Perovskite Oxide Surface: Effects on Oxygen Reduction Reaction at Elevated Temperatures
SungHyun Jeon, Wan‐Gil Jung, Wan‐Gil Jung, Hohan Bae, Sejong Ahn, Bonjae Koo, WonJeong Yu, Seunghyun Kim, DongHwan Oh, Uisik Kim, Scott A. Barnett, Jongsu Seo, Bong‐Joong Kim, WooChul Jung, WooChul Jung
Abstract
Abstract The activity and durability of chemical/electrochemical catalysts are significantly influenced by their surface environments, highlighting the importance of thoroughly examining the catalyst surface. Here, Cu‐substituted La 0.6 Sr 0.4 Co 0.2 Fe 0.8 O 3‐δ is selected, a state‐of‐the‐art material for oxygen reduction reaction (ORR), to explore the real‐time evolution of surface morphology and chemistry under a reducing atmosphere at elevated temperatures. Remarkably, in a pioneering observation, it is discovered that the perovskite surface starts to amorphize at an unusually low temperature of approximately 100 °C and multicomponent metal nanocatalysts additionally form on the amorphous surface as the temperature raises to 400 °C. Moreover, this investigation into the stability of the resulting amorphous layer under oxidizing conditions reveals that the amorphous structure can withstand a high‐temperature oxidizing atmosphere (≥650 °C) only when it has undergone sufficient reduction for an extended period. Therefore, the coexistence of the active nanocatalysts and defective amorphous surface leads to a nearly 100% enhancement in the electrode resistance for the ORR over 200 h without significant degradation. These observations provide a new catalytic design strategy for using redox‐dynamic perovskite oxide host materials.