Microstructure formation during laser powder bed fusion of Ti-22Al-25Nb with low and high pre-heating temperatures
Joachim Gussone, Marcus Willi Rackel, Silvana Tumminello, Pere Barriobero‐Vila, Frederic Kreps, Klemens Kelm, Andreas Stark, Norbert Schell, Florian Pyczak, Jan Haubrich, Guillermo Requena
Abstract
We compare microstructure formation during laser powder bed fusion (LPBF) of a Ti-22Al-25Nb alloy applying low and high pre-heating build plate temperatures. Fast cooling rates during low-temperature LPBF lead to metastable weakly ordered β phase, i.e., bcc–(Ti,Al,Nb) with pronounced <100> texture in build direction and nanosized segregations within grains elongated in the build direction. For high-temperature LPBF a Widmanstätten microstructure was observed with lenticular O phase precipitates within the β matrix. Microscopical and in situ high-energy synchrotron diffraction investigations demonstrate that the microstructure formation can be widely explained by the precipitation of O phase from supersaturated β rather than by a sequence of solid-state phase transformations, as it would be expected under thermodynamic equilibrium conditions. A detailed analysis of the microstructural gradient in the subsurface region, however, demonstrates that precipitation from metastable β cannot fully explain the observed microstructures, and that the process energy density, i.e., the intensity of the intrinsic heat treatment of LPBF, plays a relevant role. The investigation of the graded area near the surface of the LPBF materials produced with high pre-heating temperature is particularly interesting as it reveals preferred nucleation of the O phase at subgrain boundaries and dislocations.