A numerical study on fatigue strength degradation due to pitting corrosion of S355 structural steel in a marine environment
Seyed Ahmad Elahi, F. Mehri Sofiani, Somsubhro Chaudhuri, J.A. Balbín, N.O. Larrosa, Wim De Waele