Anti-corrosion performance of ethyl dimethyl propylammonium bis (trifluoromethyl sulfonyl) imide (EDMPA-TFSI) for AA3003 alloy in acid chloride solutions in the presence and absence of potassium iodide
Alexander I. Ikeuba, Brian E. Usibe, Nelson Essiet, Christopher U. Sonde, Benedict I. Ita, F. E. Abeng, Arit A. Etim
Abstract
This work aims to evaluate the anti-corrosion potential of ethyl dimethyl propylammonium bis (trifluoromethyl sulfonyl) imide (EDMPA-TFSI)-ionic liquid on AA3003 alloy in 0.5 M HCl solution in the presence and absence of potassium iodide at ambient and elevated temperatures. The corrosion inhibition of AA3003 alloy by EDMPA-TFSI in the presence of potassium iodide was evaluated using hydrogen evolution measurements at 303 K and 333 K. The results show that in the absence of potassium iodide, EDMPA-TFSI decelerates AA3003 corrosion in an acidic medium with a maximum inhibition efficiency of 93.2 % and 90.5 % obtained at 303 K and 333 K respectively. In the presence of potassium iodide, 94.7 % and 89.8 % inhibition efficiencies were obtained at 303 K and 333 K, respectively. This adsorption behavior is concordant with the Langmuir adsorption isotherm and the corrosion process in the presence of EDMPA-TFSI shows consistency with first-order reaction kinetics. New information on the application of EDMPA-TFSI as a workable corrosion inhibitor is provided herein.