Printed Organic Light-Emitting Diodes on Fabric with Roll-to-Roll Sputtered ITO Anode and Poly(vinyl alcohol) Planarization Layer
Sunyoung Sohn, Seongju Kim, Jae Won Shim, Sang Kooun Jung, Sang Kooun Jung, Sungjune Jung, Sungjune Jung
Abstract
Electronic textiles, which are a combination of fabrics and electronics, can help realize wearable electronic devices by changing the rigidity of these textiles. We demonstrate organic light-emitting diodes (OLEDs) by directly printing the emitting material on fabric substrates using the nozzle-printing technique. Printing the emitting material directly on a fabric substrate with a rough surface is difficult. To address this, we introduce a planarization layer by using a synthesized 3.5 wt % poly(vinyl alcohol) (PVA) solution. The sputtered ITO anode with the thermally annealed PVA planarization layer on a fabric substrate achieves a low sheet resistance in the range of 60–80 Ω/sq, whereas the ITO electrode without a PVA layer exhibits high sheet resistance values of 10–25 kΩ/sq. This result is because the thermally annealed PVA layer on the fabric surface has a uniform surface morphology and a water contact angle as high as 96°, thus acting as a protective layer with a waterproofing effect; in contrast, the water is completely absorbed on the rough surface without a PVA layer. The fabric-based OLEDs with a thermally annealed PVA layer exhibit a lower turn-on voltage of 3 V and higher luminance values of 5346 cd/m2 at 8 V compared with the devices without a PVA layer (7 V and 3622 cd/m2) at 18 V. These fabric-based OLEDs with a PVA planarization layer can be produced by the nozzle-printing process and can achieve selective patterning as well as direct printing of the emitting material and ITO sputtering on a fabric substrate; furthermore, they emit well even when it bent into a circle with a radius of 1 cm.