Productivity improvement in butt joining of thick stainless steel plates through the usage of activated TIG welding
Suman Saha, Bashab Chandra Paul, Santanu Das
Abstract
Abstract Activated tungsten inert gas (A-TIG) welding is one variant of conventional TIG welding where a thin layer of suitable activating flux is deposited on the parent components prior to constituting the arc in order to harness enhanced penetration. Despite several benefits, industries are still reluctant in overwhelmingly using this new variant. This article attempts to highlight the productivity benefits in employing A-TIG welding either together with or superseding TIG welding during butt joining of 10-mm-thick AISI-316L austenitic stainless steel components. Initially, three single-component fluxes (Cr 2 O 3 , Fe 2 O 3 , and SiO 2 ) are tested in forehand welding technique under varying currents but with straight polarity. Filler rod having similar metallurgical composition is also delivered during homogeneous welding. The extent of capability of each of the three fluxes is analysed by comparing the weld bead geometrical parameters (penetration, puddle width, and reinforcement) with the same obtained in conventional TIG welding under similar set of parameters. While Fe 2 O 3 and SiO 2 fluxes are found capable in enhancing penetration and reducing puddle width and heat affected zone, Cr 2 O 3 flux failed to exhibit better performance. The article further demonstrates the time saving that can be obtained by adopting flux-assisted TIG for joining 10-mm-thick plates. When joining from both the faces is allowed, about 70% less time is desired if a combination of A-TIG and TIG is employed rather than using only TIG welding. If joining from only one face is allowed, then also usage of flux can reduce welding time by 33%.