Leaching of Copper from Waste-Printed Circuit Boards (PCBs) in Sulfate Medium Using Cupric Ion and Oxygen
Yujin Park, Yuik Eom, Kyoungkeun Yoo, Manis Kumar Jha
Abstract
In the present paper, the leaching of copper from printed circuit boards (PCBs) using sulfuric acid with Cu2+ and O2 is proposed. The effects of various process parameters such as agitation speed, temperature, the type and the flow rate of gas, initial Cu2+ concentration, and pulp density were investigated to examine the dissolution behavior of Cu from PCBs in 1 mol/L sulfuric acid. The kinetic studies were performed using the obtained leaching data. The leaching rate of Cu from PCBs was found to be higher on addition of Cu2+ and O2 to the leachant in comparison with the addition of O2 or both Cu2+ and N2 in the leachant. The leaching efficiency of Cu was found to be increased with increasing agitation speed, temperature, O2 flow rate, and initial Cu2+ concentration and decreasing pulp density. The 96% of Cu leaching efficiency was obtained under the following conditions: sulfuric acid concentration, 1 mol/L; temperature, 90 °C; agitation speed, 600 rpm; pulp density, 1%; initial Cu2+ concentration, 10,000 mg/L; and O2 flow rate, 1000 cc/min. The leaching data and analyses indicate that the Cu leaching from PCBs followed the reaction-controlled model satisfactorily and determined that the activation energy was found to be 23.8 kJ/mol. Therefore, these results indicate that the sulfuric acid solution with Cu2+ and O2 as a mild leach medium without strong oxidants such as HNO3, H2O2, and Fe3+ is valid for Cu leaching from PCBs.