Achieving superior strength and conductivity for Al-Zr-Sc wires by coupling design of deformation and ageing
Siyue Fan, Jiawen Feng, Zhenhua Li, Wenlong Xiao, Peng Yan, Peng Xue, Qingwei Jiang
Abstract
Strength and electrical conductivity (EC) are key properties for heat-resistant Al-Zr-based alloy wires used as overhead transmission lines. Developing high-strength conductors with EC over 61.0% IACS has been a long-standing issue for heat-resistant Al conductive wires. In this work, a new design idea involving the coupling design of deformation and ageing was innovatively proposed to produce ultra-heat-resistant Al-0.2Zr-0.06Sc wires. The desired combination of high strength (195 ± 2 MPa) and good EC (61.2% IACS) was successfully achieved without annealing treatment. The strength residual rate of cold-drawn Al-0.2Zr-0.06Sc wire is as high as 94.0% after heat exposure of 280°C/1 h.