Rubber-based phosphaphenanthrene grafted polymer and its application to fabricate flame retardant polycarbonate blend with satisfied comprehensive mechanical properties
Anqi Liu, Yong Qiu, Lijun Qian, Yuan Meng, Hao Shang, Shuwei Liu, Wei Tang, Wang Xi, Jingyu Wang, Yajun Chen
Abstract
Grafting flame retardant groups onto common polymer molecule can be a good strategy to constructing superior flame retardant macromolecules, which provides a promising direction to fabricate fire safety polymer materials with satisfied comprehensive mechanical properties. In this thesis, a rubber-based phosphaphenanthrene grafted polymeric molecule (P-SBS) was synthesized via the grafting reaction of 9, 10-dihydro-9-oxa-10-phenanthrene-10-oxide (DOPO) with thermoplastic styrene-butadiene-styrene copolymer (SBS), and then applied to melt blending with polycarbonate (PC) to form P-SBS/PC blend with sea-island structure. The incorporated P-SBS not only brought PC much higher comprehensive flame retardancy, including higher limited oxygen index, shorter self-extinguishing time, less heat release during burning process, higher-quality char layer structure, and fewer amount of flammable volatile emission; but also endowed it with more satisfied comprehensive mechanical properties, including larger elongation at break , better anti-impact, higher flexural strength , and maintained tensile strength . By analysing burning residue, tracking thermal decomposition volatile emission, and inferring the pyrolysis route of P-SBS, the gas- and condensed-phase flame retardant mechanisms of P-SBS in suppressing the flammability of PC matrix were disclosed. The morphology analysis on the matrix fracture section and the embeded P-SBS particles before and after mechanical fracture , revealed the behavioral mechanism of P-SBS particles in improving the ductility, toughness, and stiffness of PC matrix. This study provides a beneficial reference to superior flame retardant molecule constructing and advanced flame retardant polymer material manufacturing.