Reactive Compatibilization of Polyamide 6/Olefin Block Copolymer Blends: Phase Morphology, Rheological Behavior, Thermal Behavior, and Mechanical Properties
Xintu Lin, Yuejun Liu, Xi Chen, Yincai Wu, Lingna Cui, Long Mao, Wei Zheng, Minghao Lin
Abstract
In this study, the morphology, rheological behavior, thermal behavior, and mechanical properties of a polyamide 6 (PA6) and olefin block copolymer (OBC) blend compatibilized with maleic anhydride-grafted polyethylene-octene copolymer (POE-g-MAH) were investigated. The morphological observations showed that the addition of POE-g-MAH enhanced the OBC particle dispersion in the PA6 matrix, suggesting a better interfacial compatibility between the pure PA6 and OBC. The results of the Fourier transform infrared (FTIR) spectroscopy analysis and the Molau test confirmed the compatibilization reactions between POE-g-MAH and PA6. The rheological test revealed that the melt viscosity, storage modulus (G'), and loss modulus (G") of the compatibilized PA6/OBC blends at low frequency were increased with the increasing POE-g-MAH content. The thermal analysis indicated that the addition of OBC had little effect on the crystallization behavior of PA6, while the incorporation of POE-g-MAH at high content (7 wt%) in the PA6/OBC blend restricted the crystallization of PA6. In addition, the compatibilized blends exhibited a significant enhancement in impact strength compared to the uncompatibilized PA6/OBC blend, in which the highest value of impact strength obtained at a POE-g-MAH content of 7 wt% was about 194% higher than that of pure PA6 under our experimental conditions.