Effects of Ni content on the corrosion behavior of Al<sub>0.5</sub>CoCrFeNi<sub><i>x</i></sub> high entropy alloys in acid and alkaline media
Qijuan Dong, W.L. Jia, Zequn Zhang, Dingxin Zhang, Junsheng Wu, Bowei Zhang
Abstract
Abstract The present work investigates the influence of Ni content on the microstructure evolution of Al 0.5 CoCrFeNi x high‐entropy alloys followed by the study on their corrosion behavior in acid and alkaline solutions, respectively. The microscopic characterization demonstrates that the transformation from a BCC single‐phase to a triple‐phase (BCC + FCC + B2) structure occurs with the increase of Ni content. The corrosion behavior of Al 0.5 CoCrFeNi x high‐entropy alloys was evaluated by electrochemical measurements coupled with morphology analysis. It is found that the corrosion on Al 0.5 CoCrFeNi 0 high‐entropy alloy in both acid and alkaline media is uniform due to its homogeneous microstructure. In contrast, the increase of Ni content leads to the formation of Al, Ni enriched B2 phase with lower Volta potential, causing the respective occurrence of selective dissolution in acid and preferential oxidation in alkaline on the Al 0.5 CoCrFeNi 0.2 , Al 0.5 CoCrFeNi 0.6 , and Al 0.5 CoCrFeNi 0.8 high‐entropy alloys.