Corrosion Behavior and Mechanical Properties of 30CrMnSiA High-Strength Steel under an Indoor Accelerated Harsh Marine Atmospheric Environment
Ning Li, Weifang Zhang, H. P. Xu, Yikun Cai, Xiaojun Yan
Abstract
In this work, the corrosion behavior and mechanical properties of 30CrMnSiA high-strength steel under a harsh marine atmosphere environment were systematically studied using accelerated test technology, along with corrosion kinetic analysis, microstructure and phase composition analysis, electrochemical measurements, and mechanical property tests. The influence of corrosion time on corrosion kinetics was characterized by the weight loss method. The corrosion layer and its product evolution were analyzed by SEM, EDS, XRD, and XPS. The corrosion behavior of steel was studied by a potentiodynamic polarization curve and EIS. Finally, the influence of corrosion on mechanical properties was studied by tensile and fatigue tests. The results show that 30CrMnSiA high strength steel has good corrosion resistance in a harsh marine atmosphere environment. Its corrosion behavior is cyclical: the outer rust layer exfoliated, the inner rust layer became the outer rust layer, and the matrix became inner rust due to the attack by the corrosive medium. The rust layer had a great protective effect on the matrix. The mechanical properties of 30CrMnSiA high-strength steel were reduced under the corrosive environment, and corrosion had a significant effect on its fatigue resistance.