Localized corrosion in selective laser melted SS316L in CO2 and H2S brines at elevated temperatures
Deeparekha Narayanan, Alán Martinez, Ulises Martin, Bilal Mansoor, Raymundo Case, Homero Castaneda
Abstract
at 25 °C and 125 °C were studied. Depletion of Cr/Mo was observed at the cell interiors and melt-pool boundaries (MPBs) compared to the cell boundaries. Volta potential differences obtained from scanning Kelvin probe force microscopy (SKPFM) showed that the MPBs were 8-20 mV lower than the matrix, while the cell interiors were 20-50 mV lower than the cell boundaries. Electrochemical impedance spectroscopy (EIS) and Mott-Schottky tests indicated a more defective passive film at 125 °C, and X-ray photoelectron spectroscopy (XPS) confirmed the formation of a less protective film with an increased S/O ratio at 125 °C than 25 °C. Initiation of localized corrosion was observed at the MPBs and pits formed after a week of immersion were wider by an order of magnitude at 125 °C than 25 °C, with evidence of cell-interior dissolution. While passivity was observed even at elevated temperatures, local chemical heterogeneities compromised the stability of the film and contributed to localized corrosion in SLM SS316L.