Regulating the Configurational Entropy to Improve the Thermoelectric Properties of (GeTe)1−x(MnZnCdTe3)x Alloys
Yilun Huang, Shizhen Zhi, Shengnan Zhang, Wenqing Yao, Weiqin Ao, Chaohua Zhang, Fusheng Liu, Junqin Li, Lipeng Hu
Abstract
In thermoelectrics, entropy engineering as an emerging paradigm-shifting strategy can simultaneously enhance the crystal symmetry, increase the solubility limit of specific elements, and reduce the lattice thermal conductivity. However, the severe lattice distortion in high-entropy materials blocks the carrier transport and hence results in an extremely low carrier mobility. Herein, the design principle for selecting alloying species is introduced as an effective strategy to compensate for the deterioration of carrier mobility in GeTe-based alloys. It demonstrates that high configurational entropy via progressive MnZnCdTe3 and Sb co-alloying can promote the rhombohedral-cubic phase transition temperature toward room temperature, which thus contributes to the enhanced density-of-states effective mass. Combined with the reduced carrier concentration via the suppressed Ge vacancies by high-entropy effect and Sb donor doping, a large Seebeck coefficient is attained. Meanwhile, the severe lattice distortions and micron-sized Zn0.6Cd0.4Te precipitations restrain the lattice thermal conductivity approaching to the theoretical minimum value. Finally, the maximum zT of Ge0.82Sb0.08Te0.90(MnZnCdTe3)0.10 reaches 1.24 at 723 K via the trade-off between the degraded carrier mobility and the improved Seebeck coefficient, as well as the depressed lattice thermal conductivity. These results provide a reference for the implementation of entropy engineering in GeTe and other thermoelectric materials.