Unified Modelling of Flow Stress and Microstructural Evolution of 300M Steel under Isothermal Tension
Rongchuang Chen, Shiyang Zhang, Mei Wang, Xianlong Liu, Fei Feng
Abstract
Constitutive models that reflect the microstructure evolution is of great significance to accurately predict the forming process of forging. Through thermal tension of 300M steel under various temperatures (950~1150 °C) and strain rates (0.01~10 s−1), the material flow and microstructure evolutions were investigated. In order to describe both the exponential hardening phenomenon at a higher temperature, and the softening phenomenon due to recrystallization at a lower temperature, a constitutive model considering microstructure evolution was proposed based on the Kocks–Mecking model. It was found that considering the stress-strain curve to be exponential in the work-hardening stage could improve the constitutive model prediction precision. The average error was 2.43% (3.59 MPa), showing that the proposed model was more precise than the modified Arrhenius model and the Kocks–Mecking model. The models to describe recrystallization kinetics and average grain size were also constructed. This work enabled the Kocks–Mecking model to predict stress-strain curves with a higher accuracy, and broadened the applicable range of the Kocks–Mecking model.