Excess oxygen-vacancy formed by FAST regime of direct-current electric field during flash sintering for 3 mol%–10 mol% Y2O3-doped ZrO2
Nobuhiro Morisaki, Tomoharu Tokunaga, Kiyoshi Kobayashi, Ayu Kodaira, Takahisa Yamamoto
Topics & Concepts
Materials scienceElectrical resistivity and conductivityOxygenSinteringAnalytical Chemistry (journal)ConductivityDopingAtmospheric temperature rangeMole fractionElectric fieldVacancy defectComposite materialThermodynamicsChemistryCrystallographyPhysical chemistryElectrical engineeringOptoelectronicsPhysicsOrganic chemistryChromatographyQuantum mechanicsEngineeringAdvanced ceramic materials synthesisAdvancements in Solid Oxide Fuel Cells