Analysis of crack formation during fuel cell catalyst ink drying process. Reduction of catalyst layer cracking by addition of high boiling point solvent

Naoki Hasegawa, Atsushi Kamiya, Takuro Matsunaga, Naoki Kitano, Masashi Harada

2021Colloids and Surfaces A Physicochemical and Engineering Aspects53 citationsDOI

Topics & Concepts

CatalysisMaterials scienceChemical engineeringDispersion (optics)SolventBoiling pointLayer (electronics)Particle (ecology)CrackingPlatinumBoilingComposite materialChemistryOrganic chemistryGeologyOpticsPhysicsEngineeringOceanographyFuel Cells and Related MaterialsElectrocatalysts for Energy ConversionAdvancements in Solid Oxide Fuel Cells