Hydrogen roles approaching ideal electrical and optical properties for undoped and Al doped ZnO thin films
Dung Van Hoang, Nam Hoang Vu, Nga Thi, Anh Tuấn Thanh Phạm, Trương Hữu Nguyễn, Jer‐Lai Kuo, Thắng Bách Phan, Vinh Cao Trần
Abstract
This paper distinguished hydrogen roles to improve electron mobility and carrier concentration in ZnO and Al doped ZnO sputtered films. By combining experimental evidences and theoretical results, we find out that hydrogen located at oxygen vacancy sites (HO) is the main factor gives rise to increase simultaneously mobility and carrier concentration which has not been mentioned before. Introducing appropriate hydrogen content during sputtering not only results in crystalline relaxation but also supports doping Al into ZnO, increasing carrier concentration and electron mobility in the film. First principles calculations confirmed hydrogen substitutional stability for oxygen vacancy, significantly reducing electron conductivity effective mass and hence increasing electron mobility. In particular, 0.8% hydrogen partial pressure ratio achieved 61 cm2V−1s−1 maximum electron mobility, optical transmittance above 82% in visible and near-infrared regions, and 2 × 1020 cm−3 carrier concentrations for HAl co-doped ZnO film. These values approach ideal electrical and optical properties for transparent conducting oxide films. The presence of one maximum electron mobility was attributed to competition between increasing mobility due to restoring effective electron mass and hydrogen passivation of native defects, and decreased electron mobility due to electron-phonon scattering.