High ytterbium concentration Yb/Al/P/Ce co-doped silica fiber for 1-µm ultra-short cavity fiber laser application
Qiubai Yang, Yafei Wang, Chunlei Yu, Fan Wang, Mengting Guo, Lei Zhang, Chongyun Shao, Meng Wang, Hui Shen, Yunfeng Qi, Lili Hu
Abstract
We demonstrate a high ytterbium concentration Yb/Al/P/Ce co-doped silica fiber by conventional modified chemical vapor deposition (MCVD) technology and solution doping process. The fiber has a Yb concentration of about 2.5 wt%, and the corresponding core absorption coefficient is measured to be ∼1400 dB/m at 976 nm. The gain coefficient was measured to be approximately 1.0 dB/cm. It is found that the Yb/Al/P/Ce co-doped silica shows a lower photodarkening-induced equilibrium loss of 52 dB/m at 633 nm than the Yb/Al/P co-doped silica fiber of 117 dB/m. Using the heavily Yb3+-doped silica fiber, a compact and robust ultrashort cavity single-frequency fiber laser was achieved with a maximum output power of 75 mW and a linewidth of 14 kHz. Furthermore, a compact passively mode-locked fiber laser (MLFL) with a repetition rate of 1.23 GHz was also proposed using our developed Yb-doped fiber. The laser properties of the proposed lasers were systematically investigated, demonstrating the superior performance of this fiber in terms of photodarkening resistance and ultrashort-cavity laser application. Furthermore, utilizing an all-fiber structure based on silica-based fiber offers the significant advantage of high stability and reliability.