Polyhydroxyalkanoate recovery from newly screened Bacillus sp. LPPI-18 using various methods of extraction from Loktak Lake sediment sample
Seid Mohammed, L. Bryan Ray
Abstract
BACKGROUND: Nowadays, the conventional plastic wastes are very challenging to environments and its production cost also creates an economic crisis due to petrochemical-based plastic. In order to solve this problem, the current studies were aimed at screening and characterizing these polyhydroxyalkanoate (PHA)-producing isolates and evaluating the suitability of some carbon source for newly screened PHA-producing isolates. MATERIAL AND METHODS: (AE01687) (99.10%). Paenibacillus sp. 172 (AF273740.1) was used as an outgroup. RESULTS: Bacillus sp. LPPI-18 is a gram-positive, rod-shaped, endospore former, and citrate test positive. This isolate showed positive for amylase, catalase, pectinase, and protease test. They produced intracellular PHA granules when this isolate was stained with Sudan Black B (SBB) and Nile blue A (NBA) preliminary and specific staining dyes, respectively. Both temperature and pH used to affect polyhydroxyalkanoates (PHA) productivity. Bacteria are able to reserve PHA in the form of granules during stress conditions. This isolate produces only when supplied with carbon sources. More PHA contents (PCs) were obtained from glucose, molasses, and D-fructose. In this regard, the maximum mean value of PC was obtained from glucose (40.55±0.7%) and the minimum was obtained from D-ribose (12.4±1.4%). Great variations (P≤0.05) of PCs were observed among glucose and sucrose, molasses and sucrose, and D-fructose and sucrose carbon sources for PHA productivity (PP) of cell dry weight (CDW) g/L. After extraction, PHA film was produced for this typical isolate using glucose as a sole carbon source. Fourier transform infrared spectrum was performed for this isolate and showed the feature of polyester at 1719.64 to 1721.16 wavelengths for these extracted samples. The peak of fingerprinting (band of carboxylic acid group) at this wavelength is a characteristic feature of polyhydroxybutyrate (PHB) and corresponds to the ester functional group (C=O). CONCLUSION: In this study, newly identified Bacillus sp. LPPI-18 is found to be producing biodegradable polymers that are used to replace highly pollutant conventional plastic polymers. This isolate is also used to employ certain cost-effective carbon sources for the production of PHA polymers.