SEM Evaluation of the Marginal Accuracy of Zirconia, Lithium Disilicate, and Composite Single Crowns Created by CAD/CAM Method: Comparative Analysis of Different Materials
Francesco Ferrini, Gaetano Paolone, Giovanna Laura Di Domenico, Nicolò Pagani, Enrico Gherlone
Abstract
(1) Background: The objective of this in vitro study is to evaluate the marginal accuracy of crowns created by CAD/CAM. (2) Methods: A customized chrome-cobalt (Cr-Co) implant abutment simulating a maxillary right first molar was fixed in a hemi-maxillary stone model and scanned. In total, 27 crowns were fabricated, including 9 lithium disilicate crowns, 9 composite crowns, and 9 zirconia crowns. The measurements were determined by scanning electron microscopy. Descriptive analysis was performed using the mean and standard deviation, while the Kruskal–Wallis test was performed to determine whether the marginal discrepancies were significantly different between each group (p < 0.05). (3) Results: The lowest marginal gap value was reported for zirconia (21.45 ± 12.58 µm), followed by composite (44.7 ± 24.96 µm) and lithium disilicate (62.28 ± 51.8 µm). The Kruskal–Wallis tests revealed a statistically significant difference (p-value < 0.05) in the mean marginal gaps between different materials. (4) Conclusions: The proposed digital workflow can be a viable alternative for fixed prosthetic rehabilitations. The best performance in terms of marginal gap was achieved by zirconia crowns, but all three materials demonstrate marginal closure below the clinically accepted threshold value (120 µm). Clinical significance: although significant differences were reported, the investigated CAD/CAM materials showed clinically acceptable marginal gaps.