Enhanced fatigue property by fabricating a gradient nanostructured surface layer in a reduced-activation steel
Yanyun Zhao, Mengtian Liang, Shaojun Liu, Weihua Zhang
Abstract
Reduced activation ferritic/martensitic (RAFM) steels have been selected as candidate structural materials for future advanced nuclear power systems. In the present work, the influence of a gradient nanograined surface layer on the fatigue properties of RAFM steels was studied. A gradient nanostructured (GNS) surface layer with a thickness of ∼85 μm was prepared on RAFM steel utilizing surface mechanical rolling treatment (SMRT). The mean grain size was approximate 43 nm at the topmost surface and increased gradually with depth. The results of the stress-controlled tension-compression fatigue experiments showed that the fatigue life enhanced approximately 6 times in the SMRT samples compared to the corresponding base metal counterparts. The relationship between the applied stress amplitude and the fatigue lifetime, and the fracture morphology showed that the surface strengthening and strain delocalization were caused by GNS, which suppressed surface crack initiation process, and hence the fatigue properties of RAFM steels improved. In addition, the deformation compatibility in GNS and coarse-grained boundaries leading to more dislocation interactions and accumulation during the cyclic process, also plays a crucial role in enhancing the fatigue properties of RAFM steel.