Dual function Li-reactive coating from residual lithium on Ni-rich NCM cathode material for Lithium-ion batteries
Tahir Sattar, Seong-Ju Sim, Bong‐Soo Jin, Hyun‐Soo Kim
Abstract
Abstract In this study, lithium phosphate (Li 3 PO 4 ) is coated on the surface of Ni-rich LiNi 0.91 Co 0.06 Mn 0.03 O 2 cathode material to enhance its cyclability and rate performance. The process is carried-out by achieving dual benefits, reduction of residual lithium compounds by converting them into Li 3 PO 4 coating material. The 0.1 mol.% Li 3 PO 4 (LiP) sample exhibits a capacity retention of 82% while the pristine NCM shows only 68.1% after 100 cycles. In addition, the LiP-0.1 NCM delivers high discharge capacities (161.9 mAh g −1 at 3C, 144.3 mAh g −1 at 4C and 94.6 mAh g −1 at 5C) as compared to the pristine NCM (129.3 mAh g −1 at 3C, 67.4 mAh g −1 at 4C and 33.4 mAh g −1 at 5C) in the voltage range of 3.0–4.3 V. In addition, the irreversible phase transition has also suppressed in the coated sample which is confirmed by cyclic voltammetry. Our study suggests that Li 3 PO 4 coating reduces the polarization and acts as protecting layer between the electrode and electrolyte that results in the superior electrochemical performance.