Thermal Stability and Dynamic Mechanical Analysis of Benzoylation Treated Sugar Palm/Kenaf Fiber Reinforced Polypropylene Hybrid Composites
S. Mohd Izwan, S.M. Sapuan, M.Y.M. Zuhri, Abdul Rahman Mohamed
Abstract
This research was performed to evaluate the mechanical and thermal properties of sugar palm fiber (SPF)- and kenaf fiber (KF)-reinforced polypropylene (PP) composites. Sugar palm/kenaf was successfully treated by benzoylation treatment. The hybridized bio-composites (PP/SPF/KF) were fabricated with overall 10 weight percentage (wt%) relatively with three different fibers ratios between sugar palm-treated and kenaf-treated (7:3, 5:5, 3:7) and vice versa. The investigations of thermal stability were then carried out by using diffraction scanning calorimetry (DSC) and thermogravimetry analysis (TGA). The result of a flammability test showed that the treated hybrid composite (PP/SPF/KF) was the specimen that exhibited the best flammability properties, having the lowest average burning rate of 28 mm/min. The stiffness storage modulus (E'), loss modulus (E"), and damping factor (Tan δ) were examined by using dynamic mechanical analysis (DMA). The hybrid composite with the best ratio (PP/SPF/KF), T-SP5K5, showed a loss modulus (E") of 86.2 MPa and a damping factor of 0.058. In addition, thermomechanical analysis (TMA) of the studies of the dimension coefficient (µm) against temperature were successfully recorded, with T-SP5K5 achieving the highest dimensional coefficient of 30.11 µm at 105 °C.