Effect of the Degree of Conversion on Mechanical Properties and Monomer Elution from Self-, Dual- and Light-Cured Core Composites
Branislava Petronijević Šarčev, Sebastian Baloš, Dubravka Marković, Ivan Šarčev, Marija Vukčević, Danka Labus Zlatanović, Vesna Miletić
Abstract
The objective of this work was to measure and correlate the degree of conversion (DC), mechanical properties and monomer elution from self-, dual- and light-cured core composites. Five samples of each of the following materials were prepared for each test: Clearfil (Core, Photo Core, Automix), Bisco (Core-Flo, Light-Core and Bis-Core). DC was determined using FTIR, compressive and flexural strength and modulus of elasticity using a universal testing machine and microhardness using Vickers hardness. Elution was measured using HPLC. One-way ANOVA with Tukey's post-test and Pearson's correlation were used to statistically analyze the data. DC of Clearfil-Dual (70.1%) and Clerafil-Photo (66.8%) were higher than Clearfil-Self (55.4%) and all Bisco materials (51.4-55.3%). Flexural strength of Clearfilwas higher than that of Bisco composites. The Microhardness of Clearfil-Dual (119.8VHN) and Clearfil-Photo (118.0VHN) were higher compared to other materials. The greatest elution was detected from self-cured materials. DC positively correlated to microhardness and compressive/flexural strength and negatively to BisGMA elution. Clearfil-Photo and Automix showed higher conversion, lower monomer elution and, generally, better mechanical properties. Self-cured composites should not be recommended for routine clinical use as their performance was inferior to dual- and light-cured composites. Microhardness may be used as an indicator of elution.