Effects of systematically varied thiourethane-functionalized filler concentration on polymerization behavior and relevant clinical properties of dental composites
Steven H. Lewis, Fugolin APP, S. Lam, Chérie Scanlon, Jack L. Ferracane, Carmem S. Pfeifer
Abstract
Introduction of thiourethane (TU) oligomer to resin-based dental restorative materials reduces stress and improves fracture toughness without compromising conversion. Localization of TU at the resin-filler interface via silanization procedures may lead to more substantial stress reduction and clinical property enhancements. The objective of this study was to evaluate composite properties as a function of TU-functionalized filler concentration. TU oligomers were synthesized using click-chemistry techniques and subsequently silanized to barium glass filler. Resin-based composites were formulated using varying ratios of TU-functionalized filler and conventional methacrylate-silanized barium filler. Material property testing included thermogravimetric analysis, real-time polymerization kinetics and depth of cure, polymerization stress, stress relaxation and fracture toughness. Clinical property testing included water sorption/solubility, composite paste viscosity, and gloss and surface roughness measured before and after subjecting the samples to 6 h of continuous tooth brushing in a custom-built apparatus using a toothpaste/water mixture. Increasing TU-filler in the composite resulted in as much as a 78% reduction in stress, coupled with an increase in fracture toughness. Conversion was similar for all groups. After simulated tooth brushing, gloss reduction was lower for TU-containing composites and surface roughness was less than or equal to the control.