From Solid-Solution MXene to Cr-Substituted Na<sub>3</sub>V<sub>2</sub>(PO<sub>4</sub>)<sub>3</sub>: Breaking the Symmetry of Sodium Ions for High-Voltage and Ultrahigh-Rate Cathode Performance
Hong Yu, Xiaopeng Ruan, Jinjin Wang, Zhen‐Yi Gu, Qinghua Liang, Junming Cao, Jinzhao Kang, Cheng‐Feng Du, Xing‐Long Wu
Abstract
Stabilizing Na+ accessibility at high voltage and accelerating Na+ diffusivity are pressing issues to further enhance the energy density of the Na3V2(PO4)3 (NVP) cathode for sodium-ion batteries (SIBs). Herein, by taking a V/Cr solid-solution MXene as a precursor, a facile in-situ reactive transformation strategy to embed Cr-substituted NVP (NVCP) nanocrystals in a dual-carbon network is proposed. Particularly, the substituted Cr atom triggers the accessibility of additional Na+ in NVCP, which is demonstrated by an additional reversible redox plateau at 4.0 V even under extreme conditions. More importantly, the Cr atom alters the Na+ ordering at the Na2 sites with an additional intermediate phase formation during charging/discharging, thus reducing the energy barriers for Na+ migration. As a result, Na+ diffusivity in NVCP accelerates to 2–3 orders of magnitude higher than that of NVP. Eventually, the NVCP cathode exhibits extraordinarily high-rate capability (78 mA g–1 at 200 C and 68975 W kg–1), outstanding cycle stability (over 1500 cycles at 10 C), excellent low-temperature property, and full cell performance.