Dentinal Tubule Penetration of a Calcium Silicate-Based Root Canal Sealer Using a Specific Calcium Fluorophore
Viviane Siqueira Coronas, Natália Villa, Angela Longo do Nascimento, Pedro Henrique Marks Duarte, Ricardo Abreu da Rosa, Marcus Vinícius Reis Só
Abstract
This study aimed to evaluate penetrability on dentinal tubule of a new bioceramic sealer through confocal laser scanning microscopy (CLSM). A specific fluorophore (Fluo-3) was mixed with the sealer. Forty distobuccal roots from maxillary molars were selected, and root canal preparation was carried out with Wave One Gold # 35.06 instruments. Roots were randomly assigned to 4 groups according to the filling procedures: Bioceramic/Lentulo (Sealer Plus BC); Bioceramic/EasyClean group, three activation of the sealer (3x20 s) with Easy Clean instrument; Bioceramic/Irrisonic: ultrasonic activation for 30 s; and AHplus/Lentulo: epoxy resin based sealer (AH Plus) was utilized with the same protocol as the BC/LE group. After 72 h, specimens were transversally sectioned at 2 and 7 mm from root apex and then analyzed through CLSM. Sealer penetration area on dentinal tubule was measured by Adobe Photoshop CC2018. Kruskal Wallis and Wilcoxon T tests were carried out. Penetrability results were similar for both sealers regardless of which technique was performed to activate them inside the root canal (p>0.05). It is reasonable to conclude that penetration of bioceramic and epoxy resin based sealers occurred unimpressively. The type of instrument used to activate bioceramic sealer did not affect penetrability. Fluo 3 should be recommended as the fluorophore to evaluate dentinal tubule penetration of bioceramic sealers.