Preparation, characterization, and tribological properties of silica-nanoparticle-reinforced B-N-co-doped reduced graphene oxide as a multifunctional additive for enhanced lubrication
Sang Xiong, Baosen Zhang, Shuai Luo, Hao Wu, Zhen Zhang
Abstract
Abstract Microwave-synthesized SiO 2 -reinforced B-N-co-doped reduced graphene oxide (SiO 2 -B-N-GO) nanocomposites were characterized by X-ray photon spectroscopy (XPS), X-ray diffraction (XRD), infrared (IR) spectroscopy, and transmission electron microscopy/energy dispersive X-ray (TEM/EDX) analysis. The tribological properties of the SiO 2 -B-N-GO prepared as anti-wear additives for enhanced lubrication were studied using a four-ball tester. The experiment results indicated that SiO 2 -B-N-GO exhibits excellent load-carrying, anti-wear, and anti-friction properties in a base oil, especially at the optimal concentration of additives at 0.15 wt%. The wear scar diameter decreased from 0.70 to 0.37 mm and the coefficient of friction was reduced from 0.092 to 0.070, which reductions are attributed to the formation of B-N and graphene layer tribofilms of several tens of nanometers in thickness that prevented direct contact between metals.