Effect of mechanical loading on PLGA biodegradation
Devleena Samanta, John A. Koithan, Anastasia Muliana, Matt Pharr
Abstract
Poly(lactic-co-glycolic) acid (PLGA) has been widely implemented in tissue engineering and drug delivery systems, stemming from its biocompatibility, controllable biodegradation, non-toxicity, non-immunogenicity, and tunable mechanical properties. PLGA exhibits a broad range of degradation times and modes, which can be finely tuned by adjusting various parameters, namely by altering the ratio of lactide and glycolide units, molecular weight, end group functionality, specimen geometry, processing temperature, and chemistry of the surrounding medium. To tailor the degradation profile, the in vitro profile should closely reflect the in vivo profile; however, the effects of mechanical loading coupled with hydrolysis on PLGA biodegradation are typically overlooked. To this end, this study investigates the combined effects of mechanical loading and hydrolysis at 37°C on the changes in the chemical and physical properties of PLGA as it degrades with time. We found that after several days of combined loading and hydrolysis at 37°C PLGA significantly creeps, whereas non-loaded (but hydrolyzed) specimens only slightly elongate after relatively long-term hydrolysis (∼60 days). Despite this observation and perhaps counterintuitively, the hydrolyzed non-loaded samples exhibited faster degradation than hydrolyzed loaded samples. Additionally, our studies indicated the presence of bulk erosion in hydrolyzed non-loaded samples and surface erosion in hydrolyzed loaded samples. We also observed (only) physical ageing in control samples (loaded and non-loaded samples that were not immersed in PBS but exposed to 37°C). Based on these observations, we discuss potential underlying mechanisms for the observed differences in the biodegradation behavior of PLGA specimens with and without mechanical loading.