Anaerobic Corrosion of Zero-Valent Iron at Elevated Temperatures
Adrian D. Metzgen, Andreas Dahmke, Markus Ebert
Abstract
Increasing groundwater temperatures caused by global warming, subsurface infrastructure, or heat storage projects may interfere with groundwater remediation techniques using zero-valent iron (ZVI) technology by accelerating anaerobic corrosion. The corrosion behavior of three ZVIs widely used in permeable reactive barriers (PRBs), Peerless cast iron (PL), Gotthart-Maier cast iron (GM), and an ISPAT iron sponge (IS), was investigated at temperatures between 25 and 70 °C in half-open batch reactors by measuring the volume of hydrogen gas generated. Initially, the corrosion rates of all tested ZVIs increased with temperature; at temperatures ≤40 °C, a material-specific steady state is reached, and at temperatures >40 °C, passivation causes a decrease in long-term corrosion rates. The observed corrosion behavior was therefore assumed to be superimposed by accelerating and inhibiting effects, caused by surface precipitates where the fitting of measured corrosion rates by a modeling approach, using the corroded amount of Fe0 to account for passivating minerals, yields intrinsic activation energies (Ea, ZVI) of 81, 90, and 107 kJ mol–1 for IS, GM, and PL, respectively. An increase in H2 production might not be directly transferable to an increase in general ZVI reactivity; however, the results suggest that an increase in chlorinated hydrocarbon degradation rates can be expected for ZVI-PRBs in the immediate vicinity of low-temperature underground thermal energy storages (UTESs) or in the impact areas of high-temperature UTES with temperatures of ≤40 °C.