On Strain-Hardening Behavior and Ductility of Laser Powder Bed-Fused Ti6Al4V Alloy Heat-Treated above and below the β-Transus
Emanuela Cerri, Emanuele Ghio
Abstract
Laser powder bed-fused Ti6Al4V alloy has numerous applications in biomedical and aerospace industries due to its high strength-to-weight ratio. The brittle α'-martensite laths confer both the highest yield and ultimate tensile strengths; however, they result in low elongation. Several post-process heat treatments must be considered to improve both the ductility behavior and the work-hardening of as-built Ti6Al4V alloy, especially for aerospace applications. The present paper aims to evaluate the work-hardening behavior and the ductility of laser powder bed-fused Ti6Al4V alloy heat-treated below (704 and 740 °C) and above (1050 °C) the β-transus temperature. Microstructural analysis was carried out using an optical microscope, while the work-hardening investigations were based on the fundamentals of mechanical metallurgy. The work-hardening rate of annealed Ti6Al4V samples is higher than that observed in the solution-heat-treated alloy. The recrystallized microstructure indeed shows higher work-hardening capacity and lower dynamic recovery. The Considère criterion demonstrates that all analyzed samples reached necking instability conditions, and uniform elongations (>7.8%) increased with heat-treatment temperatures.