Influence of TIG welding process parameters on microstructure and mechanical properties of as-cast Mg–8Li–3Al–2Zn-0.5Y alloy
Hongjie Liu, Jia Ma, Wencai Liu, Guohua Wu, Jiawei Sun, Xin Tong, Peijun Chen
Abstract
In this study, the feasibility of TIG welding of as-cast Mg–8Li–3Al–2Zn-0.5Y alloys was investigated, and the quality of welded joints using different welding currents was evaluated in terms of microstructural evolution and mechanical properties. The results showed that the welding position of plates was successfully welded with good formability and no obvious welding defects at the investigated processing parameters. Significant refinement of phase size was beneficial to improve the mechanical properties of the welded joints. Under the influence of heat input, the AlLi phase in the heat-affected zone dissolved into the matrix, which improved the mechanical properties of the welded joint. The ultimate tensile strength, yield strength and elongation of the welded joint at 100 A were 224.8 MPa, 177.4 MPa and 9.9%, respectively, which is 159.5%, 159% and 43.8% of the corresponding values of the base alloy in the as-cast state. The burning loss of Li element in the welded joint was effectively controlled, which confirmed the feasibility of this welding process for welding Mg–Li alloys.