On the oxidation behavior of ZrB <sub>2</sub> –SiC–VC composites
Seyed Mohammad Arab, Mehdi Shahedi Asl, Mahdi Ghassemi Kakroudi, Behnam Salahimehr, Kosar Mahmoodipour
Abstract
Abstract In this study, near‐fully dense ZrB 2 –SiC–VC (75‐20‐5 vol%) composite was manufactured through hot pressing at 1850°C under the pressure of 40 MPa for 60 min. Then the oxidation examination of the composite was carried out under different durations and temperatures. The microstructure and phase evolution after hot pressing and oxidation processes were examined by scanning electron microscopy, and X‐ray diffractometry. The VC addition led to the formation of ZrC and VSi 2 phases, which assisted the densification of the composite by removing ZrO 2 from the particles’ surface. The oxides of ZrO 2 , SiO 2 , ZrSiO 4 , V 2 O 5 , and VO 2 formed distinct layers on the sample during the oxidation at 1700°C for 4 h with a parabolic regimen and activation energy of 177.5 kJ/mol.