Study on the effect of chain extenders on aliphatic polyurethane and its application
Wenhe Ding, Hong-Yan Liu, Yanyan Bo, Siqi Zhan, Zaiqian Yu, Yuting Zhang, Ruize Yuan, Shiwei Wang, Mingyao Zhang
Abstract
Abstract Thermoplastic polyurethane (TPU) has been applied to high‐performance laminated glass depending on its high impact strength and bonding properties. The utilization of various polyurethane molecular structures in laminated glass is scarcely reported. The selection and application of chain extenders are crucial for TPU performance. In this work, aliphatic polyurethane film with high strength has been successfully synthesized, incorporating chain extender of poly(propylene glycol) bis(2‐aminopropyl ether) (PEA230). The films with melting point above 80°C were prepared by adjusting the proportion of dimethylglyoxime (DMG), while simultaneously monitoring the thermal behavior of the samples by DMA. Results indicate that combining PEA230 and DMG in a 1:1 molar ratio yields the hydrogen bonding degree of 85.77%, toughness of 43.14 MJ m 3 , and shear stress of 1.8 MPa for the polyurethane film. Subsequently, laminated glasses based on the polyurethane film with different thermal properties were constructed successfully, and their super strong impact resistance was confirmed through falling ball impact experiments.