Precipitation behavior of a new Cu-Ni-Co-Si-Fe-Mg alloy designed with low cobalt content
Liuxin Qin, Tao Zhou, Xu Wang, Yanbin Jiang, Feng Liu, Zhu Xiao, Qian Lei, Yanlin Jia, Yi Luo, Zhou Li
Abstract
A new Cu-1.5Ni-0.7Co-0.7Si-0.3Fe-0.1 Mg alloy with low cobalt content was designed. Multi-stage thermo-mechanical treatment (MTT) was used to produce the high-performance alloy with hardness of 286 HV, yield strength of 858 MPa, tensile strength of 910 MPa and electrical conductivity of 45.4 % IACS. The addition of 0.3 wt% Fe element dissolved in (Ni,Co)2Si resulted in the formation of the orthorhombic-structured δ-(Ni,Co,Fe)2Si. During MTT, the δ-(Ni,Co,Fe)2Si, (Ni,Co)2Si, β-Ni3Si, and Fe2Si precipitated successively near the deformed organization. Transmission electron microscope observations indicated that the δ-(Ni,Co,Fe)2Si precipitates showed disc-like and rod-like shapes at different orientations, respectively. A new resource-saving, high-strength and medium-conductivity Cu-Ni-Co-Si-Fe-Mg alloy was prepared by replacing an equal amount of Co element with 0.3 wt% of Fe element, reducing the amount of scarce metal Co in the alloy.