Performance and Modification Mechanism of Recycled Glass Fiber of Wind Turbine Blades and SBS Composite-Modified Asphalt
Yihua Nie, Liu Qing, Zhiheng Xiang, Shixiong Zhong, Xinyao Huang
Abstract
Efficient disposal of composite materials recycled from wind turbine blades (WTB) at end-of-life needs to be solved urgently. To investigate the modification effects and mechanism on SBS-modified asphalt of the recycled glass fiber (GF) from WTB, GF-WTB/SBS composite-modified asphalt was prepared. Dynamic shear rheometer (DSR) and bending beam rheometer (BBR) were adopted to evaluate its performance. FTIR, SEM, EDS, and AFM methods were used to assess coupling agent pretreatment effects on GF-WTB and observe the modification mechanism. The macroscopic tests show that reasonable addition of GF-WTB effectively raises the high-temperature performance and low-temperature crack resistance evaluation index k-value of SBS-modified asphalt, and the optimal content is 2 wt% GF-WTB with 4 wt% SBS. FTIR, SEM, and EDS tests show GF-WTB can be successfully grafted by UP152 coupling agent and show that adhesion of the GF-WTB to the SBS-modified asphalt can be improved. AFM observation shows SBS and GF-WTB have good compatibility, improving the asphalt elasticity and toughness. This study provides a feasible solution for environmentally friendly regeneration of the composite materials from WTB and contributes to the development of the secondary modifier of SBS-modified asphalt.