Microstructural Improvement of Eutectic Al + Mg2Si Phases on Al–Zn–Si–Mg Cast Alloy with TiB2 Particles Additions
Byung Joo Kim, Jihoon Hwang, Yong‐Ho Park, Young Cheol Lee
Abstract
In this study, the effects of adding TiB2 particles to eutectic Al + Mg2Si phases in aluminum alloys were analyzed. The eutectic Al + Mg2Si phases were modified effectively when a large amount of TiB2 was added, and changes in the shape, size, and distribution of the eutectic Al + Mg2Si phases were confirmed using a polarizing microscope and FE-SEM. The crystal structure of the TiB2 particles and Mg2Si phases were analyzed using HR-TEM, and the analysis confirmed that the TiB2 particles can act as heterogeneous nucleation sites. This paper intends to clarify the principle of phase modification of the eutectic Al + Mg2Si phases by TiB2 particles and proposes a new mechanism to improve Mg2Si phase modification when TiB2 particles are added.