Influence of electrochemical hydrogenation parameters on microstructures prone to hydrogen-induced cracking
Margo Cauwels, Robin Depraetere, Wim De Waele, Stijn Hertelé, Tom Depover, Kim Verbeken
Topics & Concepts
Hydrogen embrittlementHydrogenMaterials scienceBlistersMicrostructureSulfuric acidElectrolyteElectrochemistryCrackingStress corrosion crackingMetallurgyCorrosionChemical engineeringComposite materialChemistryElectrodeEngineeringOrganic chemistryPhysical chemistryHydrogen embrittlement and corrosion behaviors in metalsCorrosion Behavior and InhibitionFatigue and fracture mechanics