Insensitive energetic microspheres DAAF/RDX fabricated by facile molecular self-assembly
Shujie Liu, Bidong Wu, Jiani Xie, Zhimin Li, Chongwei An, Jingyu Wang, Xiaodong Li
Abstract
Insensitive energetic materials are promising in the defense weapons field. However, energetic materials still suffer from great challenges and the concern about their safety limits their utilization. In this work, insensitive energetic explosive 3,3′-diamino-4,4′-azoxyfurazan/hexahydro-1,3,5-trinitro-1,3,5-triazine (DAAF/RDX) microspheres were fabricated by self-assembly method. Rod-like DAAF/RDX was prepared by mechanical ball milling for comparison. DAAF/RDX composites with different mass ratios (90:10, 80:20, and 70:30) were obtained. The morphologies and structures of as-obtained DAAF/RDX composites were characterized by scanning electron microscopy (SEM), powder x-ray diffraction (PXRD) and fourier transform infrared spectroscopy (FT-IR). The results showed that DAAF/RDX microspheres exhibited regular shaped microspheres with sizes from 0.5 to 1.2 μm. There was no crystal transition during the modification process. The thermal properties of as-obtained materials were then evaluated by differential scanning calorimetry (DSC) and materials studio software. DAAF/RDX microspheres showed an advanced decomposition peak temperature compared with rod-like DAAF/RDX. The binding energy and peak temperature values at zero βi (TP0) of DAAF/RDX (90:10) increased by 36.77 kJ/mol, 1.6 °C, and 58.11 kJ/mol, 12.3 °C compared to DAAF/RDX (80:20) and DAAF/RDX (70:30), indicating the better thermal stability of DAAF/RDX (90:10). The characteristic drop height (H50) of DAAF/RDX (higher than 100 cm) composites was higher than that of raw RDX (25 cm), suggesting significant improvements in mechanical safety. The preparation of DAAF/RDX microspheres is promising for the desensitization of RDX and useful for the formation of other materials and future wide applications.