Estimation of Low-Cycle Fatigue Lifetime in Aluminum-Silicon-Magnesium Alloy of Cylinder Heads based on Striation Marks as Failure Features of Fracture Surfaces and Paris Crack Growth Law
Mohammad Azadi, Mahdi Samiee, Sattar Mohammadi Esfarjani
Topics & Concepts
StriationMaterials scienceFracture (geology)FractographyCylinderSolid mechanicsParis' lawAluminiumMetallurgyAlloySiliconStructural engineeringComposite materialFracture mechanicsCrack closureMechanical engineeringEngineeringFatigue and fracture mechanicsMaterial Properties and Failure MechanismsMechanical Failure Analysis and Simulation