DC Breakdown and Surface Potential Behavior of Epoxy/Al<sub>2</sub>O<sub>3</sub> Nanocomposites at Cryogenic Temperature
Tie Jiang, Xiangrong Chen, Chao Dai, Honglu Guan, Ashish Paramane
Abstract
For high temperature superconducting (HTS) dc cables, one key issue is the necessity of using polymer dielectrics with higher dielectric strength at cryogenic temperature in liquid nitrogen. Nanocomposites have played an important role in improving the dielectric properties of epoxy resin (EP). This article investigates on the dc breakdown strength and the surface potential behavior of the epoxy/Al <sub xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">2</sub> O <sub xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">3</sub> nanocomposites (0, 1, 3, 5 wt%) at the room and cryogenic temperatures. Moreover, the trap distributions are analyzed from the surface potential decay (SPD) measurement. The possible effect of the trap distributions on the dc breakdown strength is discussed with the valid results. The measurements show that the dc breakdown strength and the initial surface potential continually increased with the nanoparticle addition up to 3 wt% at both room and cryogenic temperatures, and decreased thereafter. The enhancement of the breakdown strength and the initial potential is also found at cryogenic temperature. Besides, the addition of the nanoparticles decreased the rate of SPD compared with the pure epoxy. It is proposed that the higher trap density and trap level enhances the dc breakdown strength. Interestingly, under the cryogenic environment, the nanoparticles addition significantly affects the trap distributions, which further influences the dielectric strength. The enhanced dc breakdown strength is attributed to the reduced space charge formation, the charge carrier mobility and the energy of the charge carriers within the sample bulk.